$ $ mc_fecomosi.tdb $ $*********RELEASE CANDIDATE - in publications refer to this version*********** $ $ This database is an excerpt of mc_fe_v2.011, created 2013-10-18. $ $ This database contains a selection of published thermodynamic data for steel, $ as well as newly assessed data. $ Thermodynamic parameters of mc_fecomosi have been assessed in 2012 and 2013 at TU Wien $ by Povoden-Karadeniz Erwin. $ $ ############################################################################ $ $ requires MatCalc version 5.51.0.005 or higher $ $ ############################################################################ $ $ Copyright holder and editor: Erwin Povoden-Karadeniz (erwin.povoden-karadeniz@tuwien.ac.at) $ $ You are not eligible for distributing or publishing this database or parts of it. $ $ ########################################################################### $ The following assessments are incorporated in this database: $ $ ... see list of publications in the reference section at the end of this file ... $ The following elements are included in this database: $ $ Fe, Co, Mo, Si $ This database delivers reliable results for thermodynamic equilibrium calculations $ and thermokinetic precipitation simulations in $ Si-containing carbon-free precipitation-hardening high-speed steels $ The following phases are included in this database: $ They are listed in the order of their appearance $ in part D) Thermodynamic model parameters for phases $ For their documentation see part D). $ Documentation and priority rankings suggested by the editor are visible $ after reading the database and marking the phase of interest in the databases window. $ $ LIQUID $ $ FCC_A1 $ BCC_A2 $ $ Intermetallic phases $ CO3MO LAVES_PHASE MU_PHASE_I R_PHASE SIGMA $ $***************************************************************************** $ $ A) Definition of elements $ From A. T. Dinsdale, SGTE data for pure elements (REF 0) $ $***************************************************************************** $ $Element Standard state mass [g/mol] enthalpy_298 entropy_298 ELEMENT VA VACUUM 0.0 0.00 0.00 ! ELEMENT CO HCP_A3 58.933 4765.567 30.03 ! ELEMENT FE BCC_A2 55.847 4489.0 27.2797 ! ELEMENT MO BCC_A2 95.94 4589.0 28.56 ! ELEMENT SI DIA_A4 28.0855 3217.0 18.81 ! $ $***************************************************************************** $ $ B) MatCalc specific commands $ $***************************************************************************** $ $ Defines Fe as reference element REFERENCE_ELEMENT FE ! $ $ ############################################################## $ Enthalpies of vacancy formation - FCC_A1 $ ############################################################## $ $ default is Fe PARAMETER HMVA(FCC_A1,*;0) 273.00 +175000; 6000.00 N REF:pov12 ! $ ############################################################## $ Enthalpies of vacancy formation - BCC_A2 $ ############################################################## $ $ default is Fe PARAMETER HMVA(BCC_A2,*;0) 273.00 +163000; 6000.00 N REF:pov10 ! PARAMETER HMVA(BCC_A2,MO:*;0) 273.00 +286000; 6000.00 N REF:pov10 ! $ $***************************************************************************** $ $ C) Gibbs energy functions of elements $ $***************************************************************************** $ $ ########################################################### $ SER (Standard elements references) $ ########################################################### $ FUNCTION GHSERCO 273.00 +310.241+133.36601*T-25.0861*T*LN(T) -2.6547387E-3*T**2-1.7348E-07*T**3+72526.9*T**(-1); 1768.00 Y -17197.666+253.28374*T-40.5*T*LN(T)+9.3488E+30*T**(-9); 6000.00 N REF:0 ! FUNCTION GHSERFE 273.00 +1225.7+124.134*T-23.5143*T*LN(T)-0.00439752*T**2 -5.89269E-8*T**3+77358.5*T**(-1); 1811.00 Y -25383.581+299.31255*T-46*T*LN(T)+2.2960305E+31*T**(-9); 6000.00 N REF:0 ! FUNCTION GHSERMO 273.00 -7746.302+131.9197*T-23.56414*T*LN(T) -0.003443396*T**2+5.662834E-7*T**3-1.309265E-10*T**4+65812.39*T**(-1); 2896.00 Y -30556.41+283.559746*T-42.63829*T*LN(T)-4.849315E+33*T**(-9); 5000.00 N REF:0 ! FUNCTION GHSERSI 273.00 -8162.609+137.236859*T-22.8317533*T*LN(T) -1.912904E-3*T**2-0.003552E-6*T**3+176667*T**(-1); 1687.00 Y -9457.642+167.271767*T-27.196*T*LN(T)-4.2037E+30*T**(-9); 3600.00 N REF:0 ! $ $ ########################################################### $ Gibbs energy functions other than SER $ ########################################################### $ bcc FUNCTION GCOBCC 273.00 +2938-0.7138*T+GHSERCO#; 6000.00 N REF:0 ! FUNCTION GSIBCC 273.00 +47000-22.5*T+GHSERSI#; 6000.00 N REF:0 ! $ fcc FUNCTION GCOFCC 273.00 +427.591-0.61525*T+GHSERCO#; 6000.00 N REF:0 ! FUNCTION GFEFCC 273.00 -1462.4+8.282*T-1.15*T*LN(T)+6.4E-04*T**2+GHSERFE#; 1811.00 Y -27098.266+300.25256*T-46*T*LN(T)+2.78854E+31*T**(-9); 6000.00 N REF:0 ! FUNCTION GMOFCC 273.00 +15200+0.63*T+GHSERMO#; 6000.00 N REF:0 ! FUNCTION GSIFCC 273.00 +51000-21.8*T+GHSERSI#; 6000.00 N REF:0 ! $ hcp FUNCTION GMOHCP 273.00 +3803.698+131.9197*T-23.56414*T*LN(T) -3.443396E-3*T**2+0.566283E-6*T**3 +65812*T**(-1)-0.130927E-9*T**4; 2896.00 Y -19006.41+283.559746*T-42.63829*T*LN(T) -4849.315E30*T**(-9); 5000.00 N REF:0 ! FUNCTION GNIHCP 273.00 +1046+1.2552*T+GHSERNI#; 6000.00 N REF:0 ! FUNCTION ETCFESI 273.00 +63; 6000.00 N REF:92 ! $ FUNCTION FESIW1 273.00 +10476.27; 6000.00 N REF:24 ! FUNCTION LFESIB0 273.00 -27809+11.62*T; 6000.00 N REF:24 ! FUNCTION LFESIB1 273.00 -23088; 6000.00 N REF:24 ! FUNCTION LFESIB2 273.00 +3890; 6000.00 N REF:24 ! $ FUNCTION UNDEF 273.00 +1e-8; 6000.00 N ! $ $***************************************************************************** $***************************************************************************** $ $ D) Thermodynamic model parameters for phases $ $***************************************************************************** $***************************************************************************** $ $################################################################################## $ THERMODYNAMIC PARAMETERS: LIQUID $################################################################################## $ PHASE LIQUID % 1 1.0 > >> 6 ! CONSTITUENT LIQUID : CO,FE,MO,SI : ! $------------------------------------------------------------------- $ liquid pure elements $------------------------------------------------------------------- PARAMETER G(LIQUID,CO;0) 273.00 +15085.037-8.931932*T-2.19801E-21*T**(7)+GHSERCO#; 1768.00 Y +16351.056-9.683796*T-9.3488E+30*T**(-9)+GHSERCO#; 6000.00 N REF:0 ! PARAMETER G(LIQUID,FE;0) 273.00 +12040.17-6.55843*T-3.6751551E-21*T**7+GHSERFE#; 1811.00 Y -10839.7+291.302*T-46*T*LN(T); 6000.00 N REF:0 ! PARAMETER G(LIQUID,MO;0) 273.00 +41831.347-14.694912*T+4.24519E-22*T**7+GHSERMO#; 2896.00 Y +34095.373-11.890046*T+4.849315E+33*T**(-9)+GHSERMO#; 5000.00 N REF:0 ! PARAMETER G(LIQUID,SI;0) 273.00 +50696.36-30.099439*T+2.0931E-21*T**7+GHSERSI#; 1687.00 Y +49828.165-29.559068*T+4.2037E+30*T**(-9)+GHSERSI#; 3600.00 N REF:0 ! $------------------------------------------------------------------- $ liquid binary interactions $------------------------------------------------------------------- PARAMETER L(LIQUID,CO,FE;0) 273.00 -9753.82; 6000.00 N REF:152 ! PARAMETER L(LIQUID,CO,FE;2) 273.00 +2757.96; 6000.00 N REF:152 ! PARAMETER L(LIQUID,CO,MO;0) 273.00 -68756.05+31.8*T+0.2*T*LN(T); 6000.00 N REF:77 ! PARAMETER L(LIQUID,CO,MO;1) 273.00 +2184.77+1.5*T; 6000.00 N REF:77 ! PARAMETER L(LIQUID,FE,MO;0) 273.00 -6973-0.37*T; 6000.00 N REF:12 ! PARAMETER L(LIQUID,FE,MO;1) 273.00 -9424+4.502*T; 6000.00 N REF:12 ! PARAMETER L(LIQUID,FE,SI;0) 273.00 -164435+41.977*T; 6000.00 N REF:25 ! PARAMETER L(LIQUID,FE,SI;1) 273.00 -21.523*T; 6000.00 N REF:25 ! PARAMETER L(LIQUID,FE,SI;2) 273.00 +5220+5.726*T; 6000.00 N REF:25 ! PARAMETER L(LIQUID,FE,SI;3) 273.00 -28955+26.275*T; 6000.00 N REF:25 ! PARAMETER L(LIQUID,MO,SI;0) 273.00 -146600+16.5*T; 6000.00 N REF:132 ! PARAMETER L(LIQUID,MO,SI;1) 273.00 +7100-3*T; 6000.00 N REF:132 ! PARAMETER L(LIQUID,MO,SI;2) 273.00 +8000+12*T; 6000.00 N REF:132 ! $------------------------------------------------------------------- $ liquid ternary interactions $------------------------------------------------------------------- PARAMETER L(LIQUID,CO,FE,MO;0) 273.00 +1e-8; 6000.00 N REF:pov11 ! PARAMETER L(LIQUID,CO,FE,MO;1) 273.00 -60000; 6000.00 N REF:pov13 ! PARAMETER L(LIQUID,CO,FE,MO;2) 273.00 +1e-8; 6000.00 N REF:pov11 ! PARAMETER L(LIQUID,FE,MO,SI;0) 273.00 +110000; 6000.00 N REF:23 ! $ $################################################################################## $ THERMODYNAMIC PARAMETERS: FCC_A1 $################################################################################## $ TYPE_DEFINITION ' GES A_P_D FCC_A1 MAGNETIC -3.0 0.28 ! PHASE FCC_A1 %' 2 1 1 > Face-centered cubic Austenite phase with Va on interstitial sublattice >> 6 ! CONSTITUENT FCC_A1 : CO,FE%,MO,SI : VA : ! $------------------------------------------------------------------- $ FCC_A1 endmember compounds with VA $------------------------------------------------------------------- PARAMETER G(FCC_A1,CO:VA;0) 273.00 +GCOFCC#; 6000.00 N REF:0 ! PARAMETER G(FCC_A1,FE:VA;0) 273.00 -1462.4+8.282*T-1.15*T*LN(T) +0.00064*T**2+GHSERFE#; 1811.00 Y -1713.815+0.94001*T+0.4925095E+31*T**(-9)+GHSERFE#; 6000.00 N REF:0 ! PARAMETER G(FCC_A1,MO:VA;0) 273.00 +15200+0.63*T+GHSERMO#; 5000.00 N REF:0 ! PARAMETER G(FCC_A1,SI:VA;0) 273.00 +51000-21.8*T+GHSERSI#; 3600.00 N REF:0 ! $******************** binary interactions *************************** $------------------------------------------------------------------- $ FCC_A1 binary interactions with VA $------------------------------------------------------------------- PARAMETER L(FCC_A1,CO,FE:VA;0) 273.00 -8968.75; 6000.00 N REF:152 ! PARAMETER L(FCC_A1,CO,FE:VA;2) 273.00 +3528.8; 6000.00 N REF:152 ! PARAMETER L(FCC_A1,CO,MO:VA;0) 273.00 -29557.1+10.953*T; 6000.00 N REF:78 ! PARAMETER L(FCC_A1,CO,MO:VA;1) 273.00 -1382.2+15.371*T; 6000.00 N REF:78 ! PARAMETER L(FCC_A1,CO,MO:VA;2) 273.00 -18135.4; 6000.00 N REF:78 ! PARAMETER L(FCC_A1,FE,MO:VA;0) 273.00 +28347-17.691*T; 6000.00 N REF:27 ! PARAMETER L(FCC_A1,FE,SI:VA;0) 273.00 -125248+41.116*T; 6000.00 N REF:25 ! PARAMETER L(FCC_A1,FE,SI:VA;1) 273.00 -142707.6; 6000.00 N REF:25 ! PARAMETER L(FCC_A1,FE,SI:VA;2) 273.00 +89907.3; 6000.00 N REF:25 ! PARAMETER L(FCC_A1,MO,SI:VA;0) 273.00 -60000+5*T; 6000.00 N REF:pov09 ! $******************** ternary interactions *************************** $------------------------------------------------------------------- $ FCC_A1 ternary interactions with VA $------------------------------------------------------------------- PARAMETER L(FCC_A1,CO,FE,MO:VA;0) 273.00 +60000-50*T; 6000.00 N REF:pov13 ! PARAMETER L(FCC_A1,FE,MO,SI:VA;0) 273.00 +1E-7; 6000.00 N REF:12 ! $------------------------------------------------------------------- $ FCC_A1 magnetic contribution $------------------------------------------------------------------- PARAMETER TC(FCC_A1,CO:VA;0) 273.00 +1396; 6000.00 N REF:0 ! PARAMETER BMAGN(FCC_A1,CO:VA;0) 273.00 +1.35; 6000.00 N REF:0 ! PARAMETER TC(FCC_A1,CO,FE:VA;0) 273.00 +283; 6000.00 N REF:74 ! PARAMETER TC(FCC_A1,CO,FE:VA;1) 273.00 +879; 6000.00 N REF:74 ! PARAMETER BMAGN(FCC_A1,CO,FE:VA;0) 273.00 +8.407; 6000.00 N REF:152 ! PARAMETER BMAGN(FCC_A1,CO,FE:VA;1) 273.00 -3.644; 6000.00 N REF:152 ! PARAMETER TC(FCC_A1,CO,MO:VA;0) 273.00 -3700; 6000.00 N REF:78 ! PARAMETER BMAGN(FCC_A1,CO,MO:VA;0) 273.00 -3.578; 6000.00 N REF:77 ! PARAMETER TC(FCC_A1,FE:VA;0) 273.00 -201; 6000.00 N REF:0 ! PARAMETER BMAGN(FCC_A1,FE:VA;0) 273.00 -2.1; 6000.00 N REF:0 ! $ $################################################################################## $ THERMODYNAMIC PARAMETERS: BCC_A2 $################################################################################## $ TYPE_DEFINITION & GES A_P_D BCC_A2 MAGNETIC -1.0 0.4 ! PHASE BCC_A2 %& 2 1 3 > Body-centered cubic Ferrite phase. >> 6 ! CONSTITUENT BCC_A2 : CO,FE%,MO,SI : VA : ! $------------------------------------------------------------------- $ BCC_A2 endmember compounds with VA $------------------------------------------------------------------- PARAMETER G(BCC_A2,CO:VA;0) 273.00 +GCOBCC#; 6000.00 N REF:0 ! PARAMETER G(BCC_A2,FE:VA;0) 273.00 +GHSERFE#; 6000.00 N REF:0 ! PARAMETER G(BCC_A2,MO:VA;0) 273.00 +GHSERMO#; 5000.00 N REF:0 ! PARAMETER G(BCC_A2,SI:VA;0) 273.00 +47000-22.5*T+GHSERSI#; 3600.00 N REF:0 ! $******************** binary interactions *************************** $------------------------------------------------------------------- $ BCC_A2 binary interactions with VA $------------------------------------------------------------------- PARAMETER L(BCC_A2,CO,FE:VA;0) 273.00 -26222.7+125*T-15.5020*T*LN(T) -632250*T**(-1); 6000.00 N REF:152 ! PARAMETER L(BCC_A2,CO,FE:VA;2) 273.00 +2686.79+632250*T**(-1); 6000.00 N REF:152 ! PARAMETER L(BCC_A2,CO,MO:VA;0) 273.00 +5000+7.597*T; 6000.00 N REF:77 ! PARAMETER L(BCC_A2,CO,MO:VA;1) 273.00 -19208.67; 6000.00 N REF:77 ! PARAMETER L(BCC_A2,FE,MO:VA;0) 273.00 +36818-9.141*T; 6000.00 N REF:51 ! PARAMETER L(BCC_A2,FE,MO:VA;1) 273.00 -362-5.724*T; 6000.00 N REF:51 ! PARAMETER L(BCC_A2,FE,SI:VA;0) 273.00 +4*LFESIB0#-4*FESIW1#; 6000.00 N REF:24 ! PARAMETER L(BCC_A2,FE,SI:VA;1) 273.00 +4*LFESIB1#; 6000.00 N REF:24 ! PARAMETER L(BCC_A2,FE,SI:VA;2) 273.00 +16*LFESIB2#; 6000.00 N REF:24 ! PARAMETER L(BCC_A2,MO,SI:VA;0) 273.00 -60000+5*T; 6000.00 N REF:132 ! $******************** ternary interactions *************************** $------------------------------------------------------------------- $ BCC_A2 ternary interactions with VA $------------------------------------------------------------------- PARAMETER L(BCC_A2,CO,FE,MO:VA;0) 273.00 +30000-51*T; 6000.00 N REF:pov13 ! PARAMETER L(BCC_A2,FE,MO,SI:VA;0) 273.00 +1E-8; 6000.00 N REF:12 ! $------------------------------------------------------------------- $ BCC_A2 magnetic contribution $------------------------------------------------------------------- PARAMETER TC(BCC_A2,CO:VA;0) 273.00 +1450; 6000.00 N REF:0 ! PARAMETER BMAGN(BCC_A2,CO:VA;0) 273.00 +1.35; 6000.00 N REF:0 ! PARAMETER TC(BCC_A2,FE:VA;0) 273.00 +1043; 6000.00 N REF:0 ! PARAMETER BMAGN(BCC_A2,FE:VA;0) 273.00 +2.22; 6000.00 N REF:0 ! PARAMETER TC(BCC_A2,CO,FE:VA;0) 273.00 +590; 6000.00 N REF:74 ! PARAMETER BMAGN(BCC_A2,CO,FE:VA;0) 273.00 +1.406; 6000.00 N REF:152 ! PARAMETER BMAGN(BCC_A2,CO,FE:VA;1) 273.00 -0.6617; 6000.00 N REF:152 ! PARAMETER TC(BCC_A2,CO,MO:VA;0) 273.00 -3700; 6000.00 N REF:77 ! PARAMETER BMAGN(BCC_A2,CO,MO:VA;0) 273.00 -3.445; 6000.00 N REF:77 ! PARAMETER TC(BCC_A2,CO,FE,MO:VA;0) 273.00 +1e-8; 6000.00 N REF:pov10 ! PARAMETER BMAGN(BCC_A2,CO,FE,MO:VA;0) 273.00 +1e-8; 6000.00 N REF:pov10 ! PARAMETER TC(BCC_A2,FE,MO:VA;0) 273.00 +335; 6000.00 N REF:27 ! PARAMETER TC(BCC_A2,FE,MO:VA;1) 273.00 +526; 6000.00 N REF:27 ! PARAMETER TC(BCC_A2,FE,SI:VA;1) 273.00 +8*ETCFESI#; 6000.00 N REF:24 ! $################################################################################## $ THERMODYNAMIC PARAMETERS: CO3MO $################################################################################## $ $ hcp-structured intermetallic compound (kappa) PHASE CO3MO % 2 3 1 > >> 1 ! CONSTITUENT CO3MO : CO : MO : ! PARAMETER G(CO3MO,CO:MO;0) 273.00 -47009.6+20.816*T+3*GHSERCO#+GHSERMO#; 6000.00 N REF:77 ! $ $################################################################################## $ THERMODYNAMIC PARAMETERS: LAVES_PHASE $################################################################################## $ PHASE LAVES_PHASE % 2 2 1 > MgZn2-type intermetallic phase, topologically close-packed (TCP). Low ductility and brittle fracture characteristics at low temperatures. Simplified description without distinguishing cubic C15, hexagonal C14 and dihexagonal C36 types. Optimized for use in thermokinetic precipitation simulations in austenitic stainless steel (pov12). >> 4 ! CONSTITUENT LAVES_PHASE : CO,FE%,MO,SI : CO,FE,MO%,SI : ! PARAMETER G(LAVES_PHASE,CO:CO;0) 273.00 +3*GHSERCO#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,CO:FE;0) 273.00 +2*GHSERCO#+GHSERFE#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,CO:MO;0) 273.00 +2*GHSERCO#+GHSERMO#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,CO:SI;0) 273.00 +2*GHSERCO#+GHSERSI#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,FE:CO;0) 273.00 +2*GHSERFE#+GHSERCO#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,FE:FE;0) 273.00 +3*GHSERFE#+61917; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,FE:MO;0) 273.00 -10940+2*GFEFCC#+GHSERMO#; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,FE:SI;0) 273.00 +2*GHSERFE#+GHSERSI#+100000; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,MO:CO;0) 273.00 +2*GHSERMO#+GHSERCO#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,MO:FE;0) 273.00 +2*GHSERMO#+GHSERFE#+193000; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,MO:MO;0) 273.00 +3*GHSERMO#+132120; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,MO:SI;0) 273.00 +2*GHSERMO#+GHSERSI#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,SI:CO;0) 273.00 +2*GHSERSI#+GHSERCO#+15000; 6000.00 N REF:pov10 ! PARAMETER G(LAVES_PHASE,SI:FE;0) 273.00 +2*GHSERSI#+GHSERFE#+137000; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,SI:MO;0) 273.00 +2*GHSERSI#+GHSERMO#+50000; 6000.00 N REF:pov13 ! PARAMETER G(LAVES_PHASE,SI:SI;0) 273.00 +3*GHSERSI#+170000; 6000.00 N REF:pov13 ! $----------------------Interaction parameters---------------------- PARAMETER L(LAVES_PHASE,CO,FE:*;0) 273.00 +70000; 6000.00 N REF:pov10 ! PARAMETER L(LAVES_PHASE,*:CO,FE;0) 273.00 +70000; 6000.00 N REF:pov10 ! PARAMETER L(LAVES_PHASE,CO,MO:*;0) 273.00 +70000; 6000.00 N REF:pov10 ! PARAMETER L(LAVES_PHASE,*:CO,MO;0) 273.00 +70000; 6000.00 N REF:pov10 ! PARAMETER L(LAVES_PHASE,FE,SI:MO;0) 273.00 -740000+300*T; 6000.00 N REF:pov13 ! $ $##################################################################### $ THERMODYNAMIC PARAMETERS: MU_PHASE_I $##################################################################### $ PHASE MU_PHASE_I % 4 6 1 2 4 > Hard, brittle intermetallic compound. W6Fe7-type. Important hardening phase in Fe-Co-Mo alloys. Advanced description, based on model V from ref 77. >> 4 ! CONSTITUENT MU_PHASE_I : CO,FE%,MO : CO%,FE,MO,SI : CO,FE,MO%,SI : CO,FE,MO% : ! PARAMETER G(MU_PHASE_I,CO:CO:CO:MO;0) 273.00 -130245.8+57.602*T+7*GCOFCC# +2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:77 ! PARAMETER G(MU_PHASE_I,CO:CO:MO:MO;0) 273.00 -105406.7+19.784*T +7*GCOFCC#+6*GHSERMO#; 6000.00 N REF:77 ! PARAMETER G(MU_PHASE_I,CO:MO:CO:MO;0) 273.00 -111839.1+52.818*T +6*GCOFCC#+4*GHSERMO#+2*GCOBCC#+GMOFCC#; 6000.00 N REF:77 ! PARAMETER G(MU_PHASE_I,CO:MO:MO:MO;0) 273.00 -87000+15*T +6*GCOFCC#+6*GHSERMO#+GMOFCC#; 6000.00 N REF:77 ! PARAMETER G(MU_PHASE_I,CO:MO:MO:CO;0) 273.00 +6*GCOFCC#+GMOFCC#+4*GCOBCC# +2*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:FE:FE;0) 273.00 +7*GFEFCC# +2*GHSERFE#+4*GHSERFE# +100000; 6000.00 N REF:pov13 ! PARAMETER G(MU_PHASE_I,MO:CO:CO:MO;0) 273.00 +6*GMOFCC#+GCOFCC#+2*GCOBCC# +4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:CO:MO:CO;0) 273.00 +6*GMOFCC#+GCOFCC#+2*GHSERMO# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:CO:CO;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GCOBCC# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:CO:MO:MO;0) 273.00 +6*GMOFCC#+GCOFCC#+2*GHSERMO# +4*GHSERMO#+500000; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:CO:MO;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GCOBCC# +4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:MO:CO;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GHSERMO# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:MO:FE;0) 273.00 +7*GFEFCC# +2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:MO:MO;0) 273.00 +7*GFEFCC#+6*GHSERMO# -46663-5.891*T; 6000.00 N REF:111 ! PARAMETER G(MU_PHASE_I,FE:FE:FE:MO;0) 273.00 +7*GFEFCC#+2*GHSERFE# +4*GHSERMO#-25000; 6000.00 N REF:pov13 ! PARAMETER G(MU_PHASE_I,MO:FE:FE:FE;0) 273.00 +6*GMOFCC#+GFEFCC# +2*GHSERFE#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:MO:FE:FE;0) 273.00 +6*GFEFCC#+4*GHSERFE# +2*GHSERFE#+GMOFCC#; 6000.00 N REF:pov13 ! PARAMETER G(MU_PHASE_I,FE:MO:FE:MO;0) 273.00 +6*GFEFCC#+4*GHSERMO# +2*GHSERFE#+GMOFCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:MO:MO:MO;0) 273.00 +6*GFEFCC#+6*GHSERMO# +GMOFCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:MO:MO:FE;0) 273.00 +6*GFEFCC# +GMOFCC#+4*GHSERFE# +2*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:FE:FE:MO;0) 273.00 +6*GMOFCC#+GFEFCC#+2*GHSERFE# +4*GHSERMO#+200000; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:FE:MO:FE;0) 273.00 +6*GMOFCC#+GFEFCC#+2*GHSERMO# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:FE:FE;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GHSERFE# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:FE:MO:MO;0) 273.00 +6*GMOFCC#+GFEFCC#+2*GHSERMO# +4*GHSERMO#+200000; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:FE:MO;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GHSERFE# +4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:MO:FE;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GHSERMO# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:MO:MO;0) 273.00 +65000+7*GMOFCC# +6*GHSERMO#; 6000.00 N REF:77 ! PARAMETER G(MU_PHASE_I,CO:CO:CO:FE;0) 273.00 +7*GCOFCC# +2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:CO:FE:FE;0) 273.00 +7*GCOFCC# +6*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:FE:CO:FE;0) 273.00 +6*GCOFCC#+4*GHSERMO# +2*GCOBCC#+GMOFCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:FE:FE:FE;0) 273.00 +6*GCOFCC#+6*GHSERMO# +GMOFCC#; 6000.00 N REF:pov11 ! $ PARAMETER G(MU_PHASE_I,CO:FE:FE:CO;0) 273.00 +6*GCOFCC#+GFEFCC# +4*GCOBCC# +2*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:CO:CO:FE;0) 273.00 +6*GFEFCC#+GCOFCC# +2*GCOBCC# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:CO:FE:CO;0) 273.00 +6*GFEFCC#+GCOFCC# +2*GHSERFE# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:CO:CO;0) 273.00 +6*GFEFCC#+GFEFCC# +2*GCOBCC# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:CO:FE:FE;0) 273.00 +6*GFEFCC#+GCOFCC# +2*GHSERFE# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:CO:FE;0) 273.00 +6*GFEFCC#+GFEFCC# +2*GCOBCC# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:FE:CO;0) 273.00 +6*GFEFCC#+GFEFCC# +2*GHSERFE# +4*GCOBCC#; 6000.00 N REF:pov11 ! $ PARAMETER G(MU_PHASE_I,CO:CO:MO:FE;0) 273.00 +7*GCOFCC# +2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:CO:FE:MO;0) 273.00 -100000+7*GCOFCC# +4*GHSERMO#+2*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:MO:CO:FE;0) 273.00 +6*GCOFCC# +GMOFCC#+2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:FE:CO:MO;0) 273.00 +6*GCOFCC# +GFEFCC#+2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:MO:FE:CO;0) 273.00 +6*GCOFCC# +GMOFCC#+2*GHSERFE#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:FE:MO:CO;0) 273.00 +6*GCOFCC# +GFEFCC#+2*GHSERMO#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:CO:CO:FE;0) 273.00 +6*GMOFCC# +GCOFCC#+2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:CO:CO:MO;0) 273.00 +6*GFEFCC# +GCOFCC#+2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:MO:CO:CO;0) 273.00 +6*GFEFCC# +GMOFCC#+2*GCOBCC#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:FE:CO:CO;0) 273.00 +6*GMOFCC# +GFEFCC#+2*GCOBCC#+4*GCOBCC#; 6000.00 N REF:pov09 ! $ PARAMETER G(MU_PHASE_I,MO:MO:CO:FE;0) 273.00 +7*GMOFCC# +2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:MO:FE:CO;0) 273.00 +7*GMOFCC# +2*GHSERFE#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:CO:MO:FE;0) 273.00 +6*GMOFCC# +GCOFCC#+2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:FE:MO:CO;0) 273.00 +6*GMOFCC# +GFEFCC#+2*GHSERMO#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:CO:FE:MO;0) 273.00 +6*GMOFCC# +GCOFCC#+2*GHSERFE#+4*GHSERMO#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:FE:CO:MO;0) 273.00 +6*GMOFCC# +GFEFCC#+2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:MO:MO:FE;0) 273.00 +6*GCOFCC# +GMOFCC#+2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:MO:MO:CO;0) 273.00 +6*GFEFCC# +GMOFCC#+2*GHSERMO#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:CO:MO:MO;0) 273.00 -95000+6*GFEFCC# +GCOFCC#+2*GHSERMO#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:FE:MO:MO;0) 273.00 +6*GCOFCC# +GFEFCC#+2*GHSERMO#+4*GHSERMO#; 6000.00 N REF:pov09 ! $ PARAMETER G(MU_PHASE_I,FE:FE:CO:MO;0) 273.00 +7*GFEFCC# +2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:FE:MO:CO;0) 273.00 +7*GFEFCC# +2*GHSERMO#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:MO:FE:CO;0) 273.00 +6*GFEFCC# +GMOFCC#+2*GHSERFE#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:CO:FE:MO;0) 273.00 +6*GFEFCC# +GCOFCC#+2*GHSERFE#+4*GHSERMO#-10000; 6000.00 N REF:pov13 ! PARAMETER G(MU_PHASE_I,FE:CO:MO:FE;0) 273.00 +6*GFEFCC# +GCOFCC#+2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,FE:MO:CO:FE;0) 273.00 +6*GFEFCC# +GMOFCC#+2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:FE:FE:MO;0) 273.00 +6*GCOFCC# +GFEFCC#+2*GHSERFE#+4*GHSERMO#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:FE:FE:CO;0) 273.00 +6*GMOFCC# +GFEFCC#+2*GHSERFE#+4*GCOBCC#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,MO:CO:FE:FE;0) 273.00 +6*GMOFCC# +GCOFCC#+2*GHSERFE#+4*GHSERFE#; 6000.00 N REF:pov09 ! PARAMETER G(MU_PHASE_I,CO:MO:FE:FE;0) 273.00 +6*GCOFCC# +GMOFCC#+2*GHSERFE#+4*GHSERFE#; 6000.00 N REF:pov09 ! $ $----------------------Interaction parameters---------------------- $ PARAMETER L(MU_PHASE_I,CO,FE:CO:MO:MO;0) 273.00 -60000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO,FE:CO:MO:MO;1) 273.00 -60000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO,FE:FE:MO:MO;0) 273.00 +1e-8; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO,FE:CO:MO:FE;0) 273.00 +1e-8; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO,FE:CO:MO:CO;0) 273.00 +1e-8; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO,FE:CO:MO:FE,MO;0) 273.00 0; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,FE:CO:MO:FE,MO;0) 273.00 +200000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO:FE:MO:FE,MO;0) 273.00 +200000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO:CO:MO:FE,MO;0) 273.00 +200000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,FE:FE:MO:FE,MO;0) 273.00 +200000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,FE:CO:FE,MO:MO;0) 273.00 -175000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO:FE:FE,MO:MO;0) 273.00 -175000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,FE:CO:CO,MO:MO;0) 273.00 -175000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO:FE:CO,MO:MO;0) 273.00 -175000; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,CO:CO,MO:CO:MO;0) 273.00 -4263+10*T; 6000.00 N REF:77 ! PARAMETER L(MU_PHASE_I,CO:CO,MO:MO:MO;0) 273.00 -4263+10*T; 6000.00 N REF:77 ! PARAMETER L(MU_PHASE_I,CO:CO:CO,MO:MO;0) 273.00 -8141+20*T; 6000.00 N REF:77 ! PARAMETER L(MU_PHASE_I,CO:MO:CO,MO:MO;0) 273.00 -8141+20*T; 6000.00 N REF:77 ! $ $ PARAMETER WITH SILICON $ PARAMETER G(MU_PHASE_I,MO:SI:SI:MO;0) 273.00 +6*GMOFCC#+GSIFCC#+2*GSIBCC# +4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:MO:MO;0) 273.00 +6*GMOFCC#+GSIFCC#+2*GHSERMO# +4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:SI:MO;0) 273.00 +6*GMOFCC#+GMOFCC#+2*GSIBCC# +4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:SI:FE;0) 273.00 +6*GFEFCC#+GSIFCC# +2*GSIBCC# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:FE:FE;0) 273.00 +6*GFEFCC#+GSIFCC# +2*GHSERFE# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:SI:FE;0) 273.00 +6*GFEFCC#+GFEFCC# +2*GSIBCC# +4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:SI:FE;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GSIBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:SI:MO;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GSIBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:SI:FE;0) 273.00 +7*GMOFCC# +2*GSIBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:MO:FE;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:FE:MO;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GHSERFE#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:FE:SI:MO;0) 273.00 +6*GMOFCC# +GFEFCC#+2*GSIBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:MO:MO;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GHSERMO#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:SI:MO;0) 273.00 +7*GFEFCC# +2*GSIBCC#+4*GHSERMO#-400000+32*T; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:FE:MO;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GHSERFE#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:MO:FE;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GHSERMO#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:MO:SI:FE;0) 273.00 +6*GFEFCC# +GMOFCC#+2*GSIBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:FE:FE;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GHSERFE#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:SI:CO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GSIBCC# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:CO:CO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GCOBCC# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:CO:SI:CO;0) 273.00 +6*GCOFCC# +GCOFCC#+2*GSIBCC# +4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:SI:FE;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GSIBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:SI:CO;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GSIBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! $ PARAMETER G(MU_PHASE_I,CO:CO:SI:FE;0) 273.00 +7*GCOFCC# +2*GSIBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:CO:FE;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:FE:CO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GHSERFE#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:FE:SI:CO;0) 273.00 +6*GCOFCC# +GFEFCC#+2*GSIBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:CO:CO;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GCOBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:FE:SI:CO;0) 273.00 +7*GFEFCC# +2*GSIBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:FE:CO;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GHSERFE#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:SI:CO:FE;0) 273.00 +6*GFEFCC# +GSIFCC#+2*GCOBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,FE:CO:SI:FE;0) 273.00 +6*GFEFCC# +GCOFCC#+2*GSIBCC#+4*GHSERFE#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:FE:FE;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GHSERFE#+4*GHSERFE#; 6000.00 N REF:pov11 ! $ PARAMETER G(MU_PHASE_I,MO:SI:SI:CO;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GSIBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:SI:MO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GSIBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:MO:SI:CO;0) 273.00 +7*GMOFCC# +2*GSIBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:MO:CO;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GHSERMO#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:CO:MO;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:CO:SI:MO;0) 273.00 +6*GMOFCC# +GCOFCC#+2*GSIBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:MO:MO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GHSERMO#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:CO:SI:MO;0) 273.00 -400000+32*T+7*GCOFCC# +2*GSIBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:CO:MO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GCOBCC#+4*GHSERMO#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:SI:MO:CO;0) 273.00 +6*GCOFCC# +GSIFCC#+2*GHSERMO#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:MO:SI:CO;0) 273.00 +6*GCOFCC# +GMOFCC#+2*GSIBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,MO:SI:CO:CO;0) 273.00 +6*GMOFCC# +GSIFCC#+2*GCOBCC#+4*GCOBCC#; 6000.00 N REF:pov11 ! $ PARAMETER G(MU_PHASE_I,FE:CO:SI:MO;0) 273.00 +6*GFEFCC# +GCOFCC#+2*GSIBCC#+4*GHSERMO#-400000+32*T; 6000.00 N REF:pov11 ! PARAMETER G(MU_PHASE_I,CO:FE:SI:MO;0) 273.00 +1*GFEFCC# +6*GCOFCC#+2*GSIBCC#+4*GHSERMO#-400000+32*T; 6000.00 N REF:pov11 ! $ PARAMETER L(MU_PHASE_I,CO:CO,SI:MO:MO;0) 273.00 +1e-8; 6000.00 N REF:pov11 ! PARAMETER L(MU_PHASE_I,FE:CO,SI:MO:MO;0) 273.00 +1e-8; 6000.00 N REF:pov11 ! $ $################################################################################## $ THERMODYNAMIC PARAMETERS: R_PHASE $################################################################################## $ PHASE R_PHASE % 3 27 14 12 > Topologically close-packed structure, closely related to Sigma and Mu-Phase. >> 2 ! CONSTITUENT R_PHASE : FE : MO : FE,MO,SI : ! PARAMETER G(R_PHASE,FE:MO:FE;0) 273.00 +27*GFEFCC#+14*GHSERMO# +12*GHSERFE#-77487-50.486*T; 6000.00 N REF:111 ! PARAMETER G(R_PHASE,FE:MO:MO;0) 273.00 +27*GFEFCC#+26*GHSERMO# +313474-289.472*T; 6000.00 N REF:111 ! PARAMETER G(R_PHASE,FE:MO:SI;0) 273.00 +14*GHSERMO#+27*GFEFCC# +12*GSIBCC#-1000000; 6000.00 N REF:pov13 ! PARAMETER G(R_PHASE,FE:MO:FE,SI;0) 273.00 -2000000; 6000.00 N REF:pov13 ! $ $################################################################################## $ THERMODYNAMIC PARAMETERS: SIGMA $################################################################################## $ PHASE SIGMA % 3 8 4 18 > Intermetallic transition elements compound with broad solid solubility range. Tetragonal with five non-equivalent sites. A simplified 3-sublattice description is used. Hard and brittle topologically close-packed (TCP) precipitates. >> 4 ! CONSTITUENT SIGMA : CO,FE%:MO:CO,FE,MO,SI :! PARAMETER G(SIGMA,CO:MO:CO;0) 273.00 -130932.67+240.554*T+8*GCOFCC# +4*GHSERMO#+18*GCOBCC#; 6000.00 N REF:77 ! PARAMETER G(SIGMA,CO:MO:FE;0) 273.00 +8*GCOFCC#+4*GHSERMO#+18*GHSERFE#; 6000.00 N REF:pov10 ! PARAMETER G(SIGMA,CO:MO:MO;0) 273.00 -87868.24+14.662*T+8*GCOFCC#+22*GHSERMO#; 6000.00 N REF:77 ! PARAMETER G(SIGMA,CO:MO:SI;0) 273.00 +8*GCOFCC#+4*GHSERMO#+18*GSIBCC#; 6000.00 N REF:pov10 ! PARAMETER G(SIGMA,FE:MO:CO;0) 273.00 +8*GFEFCC#+4*GHSERMO#+18*GCOBCC#; 6000.00 N REF:pov11 ! PARAMETER G(SIGMA,FE:MO:FE;0) 273.00 -1813-27.272*T+8*GFEFCC# +4*GHSERMO#+18*GHSERFE#; 6000.00 N REF:27 ! PARAMETER G(SIGMA,FE:MO:MO;0) 273.00 +83326-69.618*T+8*GFEFCC#+22*GHSERMO#; 6000.00 N REF:27 ! PARAMETER G(SIGMA,FE:MO:SI;0) 273.00 +8*GFEFCC#+4*GHSERMO#+18*GSIBCC#-1300000+300*T; 6000.00 N REF:pov13 ! $----------------------Interaction parameters---------------------- PARAMETER L(SIGMA,CO:MO:CO,MO;0) 273.00 -157492.37; 6000.00 N REF:77 ! PARAMETER L(SIGMA,FE:MO:FE,MO;0) 273.00 +222909; 6000.00 N REF:27 ! $ $***************************************************************************** $ $ E) List of references $ $***************************************************************************** $ A00201-0 unary A.T. Dinsdale, SGTE Data of pure elements, CALPHAD, Vol. 15, No. 4, pp 317-425, 1991. A00040-12 Al-C-Cr-Cu-Fe-Mn-Ni-Si... J. Miettinen, Thermodynamic substitutional solution data for steels, Report TKK-MK-76, pp 1-24, 1999. A00034-23 Cr-Cu-Fe-Mn-Mo-Ni-Si-V... J. Miettinen, Approximate thermodynamic solution phase data for steels, CALPHAD, Vol. 22, No. 2, pp 275-300, 1998. A00010-24 C-Fe-Si J. Lacaze, B. Sundman, An assessment of the Fe-C-Si system, Metall. Trans., Vol. 22A, pp 2211-2223, 1991. A00028-25 C-Fe-Si J. Miettinen, Reassessed thermodynamic solution phase data for ternary Fe-Si-C system, CALPHAD, Vol. 22, No. 2, pp 231-256, 1998. A00015-27 C-Fe-Mo J. O. Andersson, A termodynamic evaluation of the Fe-Mo-C system, CALPHAD, Vol. 12, No. 1, pp 9-23, 1988. 41 Fe-Mo-Ni K. Frisk, Trita-Mac-0428, Mat. Res. Centre, Royal Inst. of Tech., Stockholm, 1990. A00053-51 C-Cr-Fe-Mo M. Hillert, C. Qiu, A reassessment of the Fe-Cr-Mo-C system, J. Phase Equilib., Vol. 13, No. 5, pp 512-521, 1992. A00136-74 Fe-Co A.F. Guillermet, Critical evaluation of the thermodynamic propereties of the iron-cobalt system, High Temp.-High Press., Vol.19, pp 477-499, 1987. A00139-77 Co-Mo A.V. Davydov, U.R. Kattner, Revised thermodynamic description for the Co-Mo system (short communications), J. Phase Equilib., Vol.24, pp 209-211, 2003. A00140-78 Co-Mo A.V. Davydov, U.R. Kattner, Thermodynamic assessment of the Co-Mo system, J. Phase Equilib., Vol. 20, pp 5-16, 1999. 92 bin, tern N. Saunders, COST 507: Thermochemical database for light metal alloys, Vol. 2, pp 23-27, 1998. A00216-111 Cr-Fe-Mo J-O. Andersson, N. Lange, An experimental study and a thermodynamic evaluation of the Fe-Cr-Mo system, Metall. Trans. A, Vol. 19A, No. 6, pp 1385-1394, 1988. A00221-132 Mo-Si-Al Y. Liu, G. Shao, P. Tsakiropoulos, Thermodynamic reassessment of the Mo-Si and Al-Mo-Si systems, Intermet., Vol. 8, pp 553-962, 2000. 152 Fe-Co I. Ohnuma, H. Enoki, O. Ikeda, R. Kainuma, H. Ohtani, B. Sundman, K. Ishida, Phase equilibria in the Fe-Co binary system, Acta mater., Vol. 50, pp 379-393, 2002. pov09 E. Povoden-Karadeniz, unpublished, 2009. pov10 E. Povoden-Karadeniz, unpublished, 2010. pov11 E. Povoden-Karadeniz, unpublished, 2011. pov12 E. Povoden-Karadeniz, unpublished, 2012. pov13 E. Povoden-Karadeniz, unpublished, 2013.